1.6582 / 34CrNiMo6 Round / Square / Flat bars

34CrNiMo6 Steel

Round Bar

Size: Dia.10-300mm

Length: 3,000-10,000mm(can be Customized)

Payment Terms:T/T ,L/C

Forged steel round bar 34CrNiMo6

Process: EAF + LF + VD + Forged + Heat Treatment (optional)

SEND EMAIL GET PRICE

1.6582 / 34CrNiMo6 bar

DIN 1.6582 / 34CrNiMo6 Steel is an important alloy engineering steel grade as per DIN Germany standard. It has high strength,high toughness and good hardenability. DIN 1.6582 steel has the stability of resistance to overheating,but the white sensitivity of 34CrNiMo6 is high. It also has the temper brittleness,so the weldability is poor. This steel needs the high temperature preheating before welding,in order to eliminate the stress after welding processing.

Chemical Composition

C: 0.30-0.38; Si: max0.40; Mn: 0.50-0.80; P: max0.025; S: max0.035;

Cr: 1.30-1.70; Ni: 1.30-1.70; Mo: 0.15-0.30;

Equivalent Grades

AISI/ASTM: 4340

BS: 817M40 / EN24

JIS: SNCM447

Form of 1.6582 Steel

Round / Square / Flat Bars, Shafts, Rollers, Blocks

Size of 34CrNiMo6 Steel

– As Forged

Round bar

Size: Dia.80-1,000mm

Length: 3,000-10,000mm

Square bar

Size: 150×150-600×600mm

Length: 3,000-8,000mm

(Forged Flat Bars, Shafts, Rollers and Blocks can be Customized)

– As Rolled

Round Bar

Size: Dia.10-300mm

Length: 3,000-10,000mm(can be Customized)

Surface Condition

Black, Rough Machined, Turned,

Hardness of 1.6582 Steel

Annealed (+A): max 269HB

Mechanical Properties of 1.6582 / 34CrNiMo6 (+QT)

Tensile strength: 980MPa

Yield point: 835MPa

Percentage reduction of area after fracture: 55%

Elongation after fracture: 12%

Impact test: 45J(+20°C)

Quenched and Tempered (+QT) of 34CrNiMo6 Steel

1. Heat din 1.6582 steel slowly to the temperature of 850°C;

2. Soak at this hardening temperature quench in oil;

3. Temper as soon as 34CrNiMo6 steel reach room temperature.

4. Heat uniformly to the suitable temperature;

5. Withdraw from the furnace and cool in the air.

6. The usual tempering temperature is 600°C which depending on the actual requirements.

Applications of din 1.6582 / 34CrNiMo6 Steel

34CrNiMo6 steel is used to make tools which demands good plasticity and high strength. It is usually selected to make the big size and important parts,such as heavy machinery axle,turbine shaft larger than 250 mm in diameter,blade,high load of transmission parts,fasteners,crank shafts,gears,etc. In addition,din 1.6582 steel grade can be used to make special performance requirements of the important parts.